Great Chemical Resistance Perfluoroelastomer Compound
Mehlala ea Stock e Mahala ebile e Fumaneha
FUDI e fana ka mefuta e meraro eaperfluoroelastomer ffkmmotsoako & ffkm polymer.
A. E na le mocheso o pharaletseng ka ho fetisisa oa ho sebetsa le ho hanyetsa ka bophara ho mecha ea litaba ea lik'hemik'hale.
Likaroloana
● Ho hanyetsa ka mokhoa o tsotehang mocheso o phahameng ho fihlela ho 300-320 ℃
● Ho hanyetsa lik'hemik'hale tse mabifi;
● Ho hanyetsa mouoane ho ikhethang;
● Khatello e ikhethang e behiloeng esita le ka mocheso o phahameng haholo;
● Ho sebetsa ka theknoloji e tloaelehileng ea fluoroelastomer ho lisebelisoa tsa rabara tse tloaelehileng.
● Theko ke eona e turang ka ho fetisisa.
Kopo
Li-O-rings, litiiso, diaphragm le likarolo tse ling tse sebelisoang indastering ea ts'ebetso.
MOQ
300 grams
Lintlha bakeng sa litšupiso
| Ho hanyetsa mocheso | |
| Mocheso botsofali 70 h @ 280 ℃ | |
| 100% Modulus Mpa | 9.5 |
| Matla a tiileng Mpa | 19.5 |
| Elongation nakong ea khefu% | 215 |
| Hardness Shore A | 72 |
| Mocheso botsofali 70 h @ 300 ℃ | |
| 100% Modulus Mpa | 7.5 |
| Matla a tiileng Mpa | 17 |
| Elongation nakong ea khefu% | 260 |
| Hardness Shore A | 72 |
| Mocheso botsofali 70 h @ 316 ℃ | |
| 100% Modulus Mpa | 6.5 |
| Matla a tiileng Mpa | 14 |
| Elongation nakong ea khefu% | 320 |
| Hardness Shore A | 72 |
B. E na le mocheso o fokolang oa ho sebetsa le ho hanyetsa ka ho fetisisa ho mecha ea litaba ea lik'hemik'hale.
Likaroloana
● Ho hanyetsa ka tsela e ikhethang ho mocheso o phahameng ho fihlela ho 250 ~ 260 ℃
● Ho hanyetsa lik'hemik'hale tse mabifi;
● Ho hanyetsa mouoane ho ikhethang;
● Khatello e ikhethang e behiloeng esita le ka mocheso o phahameng haholo;
● Theko e tlase ho feta grade A.
Kopo
Li-O-rings, litiiso, diaphragm le likarolo tse ling tse sebelisoang tikolohong e thata.
MOQ
300 grams
Lintlha bakeng sa litšupiso
| Hardness Shore A | 74 |
| Matla a khoheli / | 1.99 |
| Matla a tiileng Mpa | 24.5 |
| 100% Modulus Mpa | 7.5 |
| Elongation % | 200 |
| Compress sete 72 h @ 200 ℃ | 18.1 |
| Compress sete 72 h @ 230 ℃ | 26.7 |
Ho hanyetsa lik'hemik'hale (Bakeng sa Ketone, Ester, Ether)
| Lik'hemik'hale | Temp | Fetoha kamora lihora tse 168 (%) | Fetoha kamora lihora tse 500 (%) |
| Acetone | 40 ℃ | 2.5 | 3.3 |
| Methyl ethyl ketone | 2.2 | 3.2 | |
| Isophorone | 0.1 | 0.5 | |
| Ethyl acetate | 3.1 | 3.8 | |
| Dioxane | 1.2 | 2.0 | |
| Methyl isobuthyl ketone | 1.2 | 2.0 | |
| Acetylacetone | 0.8 | 1.3 | |
| Buthyl acetate | 1.5 | 2.5 | |
| Diethyl ether | 25 ℃ | 2.6 | 4.3 |
C. E na le mocheso o fokolang oa mocheso oa ho sebetsa le ho hanyetsa hantle mecha ea litaba ea lik'hemik'hale.
Likaroloana
● Ho hanyetsa ka tsela e ikhethang ho mocheso o phahameng ho fihlela ho 240 ℃
● Ho hanyetsa lik'hemik'hale tse mabifi;
● Ho hanyetsa mouoane ho ikhethang;
● Khatello e ikhethang e behiloeng esita le ka mocheso o phahameng haholo;
● Ho sebetsa ka theknoloji e tloaelehileng ea fluoroelastomer ho lisebelisoa tse tloaelehileng tsa rabara.
● Theko e tlaase ka ho fetisisa.
Lintlha bakeng sa litšupiso
| Moea o chesang o tsofala | 300℃×24Hrs | GB/T 3512-2014 | |||
| Matla a tšepe | % | -18.1 | |||
| Elongation | % | 17.1 | |||
| Ho fetoha ho thata | 0.2 | ||||
| Compress set | 23℃×70Hrs | GB/T 7759.1-2015 | |||
| Compress set | % | 11.2 | |||
| Compress set | 204℃×70Hrs | GB/T 7759.1-2015 | |||
| Compress set | % | 22.7 | |||
| Compress set | 250℃×70Hrs | GB/T 7759.1-2015 | |||
| Compress set | % | 33.2 | (Ho na le mapheo) | ||
| Fule RP-3 | 150℃×24Hrs | GB/T 1690-2010 | |||
| Matla a tšepe | % | -14.3 | |||
| Elongation | % | 5.8 | |||
| Ho fetoha ho thata | -2 | ||||
| Ho fetoha ha molumo | % | 4.6 | |||
| Mocheso o tlase | GB/T 15256-2014 | ||||
| Brittle mocheso | ℃ | -30 |